Water resistant cellulose acetate based photopolymer for recording of volume phase holograms

The development of environmentally robust photosensitive materials for holographic recording is crucial for applications such as outdoor LED light redirection, holographic displays and holographic sensors. Despite the progress in holographic recording materials development, their sensitivity to humidity remains a challenge and protection from the environment is required. One approach to solving this challenge is to select substrate such as cellulose acetate, which is water resistant. This work reports the development of a cellulose-based photopolymer with sensitivity of 3.5 cm²/mJ and refractive index modulation of 2.5 × 10⁻³ achieved in the transmission mode of recording. The suitability for holographic recording was demonstrated by recording gratings with the spatial frequency of 800 linepairs/mm. The intensity dependence of the diffraction efficiency of gratings recorded in 70 µm thick layers was studied and it was observed that the optimum recording intensity was 10 mW/cm² . The robustness of the structures was studied after immersing the layer in water for one hour. It was observed that the diffraction efficiency and the surface characteristics measured before and after exposure to water remain unchanged. Finally, the surface hardness was characterized and was shown to be comparable to that of glass and significantly higher than the one of PVA-based acrylamide photopolymer.