Modeling the degradation/recovery of short-circuit current density in perovskite and thin film photovoltaics

Pezhman Darvishzadeh, Ghufran Redzwan, Razi Ahmadi, Nima E. Gorji

Research output: Contribution to journalArticlepeer-review

Abstract

A time-dependent approach has been developed for modeling the degradation and recovery rate of short-circuit current density in thin film and perovskite solar cells. A set of six different equations has been derived by fundamentally relating the carrier collection efficiency to the defect/trap creation/annihilation kinetics. The distribution and concentration of defects or traps across the absorber layer of a cell vary under aging conditions. As a result, the carrier collection efficiency changes due to distorted diffusion length and depletion width at the junction. These parameters are both related to defect/trap densities by reverse square 1/N(t). We applied our modeling on the experimental data reported in the literature on degradation/recovery of CdTe, CIGS, CZTS and perovskite solar cells with various architectures and prepared through different fabrication details. These devices were aged under elevated temperature, prolonged irradiation or moisture. The aging effect was taken as a change in shallow/deep defect density or trap density at mid-gap. A good fit has been obtained by setting fitting parameters in a reasonable range. These include the initial defect density, N0, and degradation time constant, τ0, of a typical defect increment profile given by N(t)=N0(1 + t/t0)1/2θ. It was shown that opposite to conventionally believed, the defect density variation may significantly change the current density of the cell even if the absorber layer's thickness is kept constant. This has been occasionally observed by aging techniques using different stress conditions.

Original languageEnglish
Pages (from-to)247-252
Number of pages6
JournalOrganic Electronics
Volume43
DOIs
Publication statusPublished - 1 Apr 2017
Externally publishedYes

Keywords

  • Degradation
  • Modeling
  • Perovskite
  • Recovery
  • Short-circuit current density
  • Solar cell
  • Thin films
  • Time-dependent

Fingerprint

Dive into the research topics of 'Modeling the degradation/recovery of short-circuit current density in perovskite and thin film photovoltaics'. Together they form a unique fingerprint.

Cite this