TY - JOUR
T1 - Evaluation of the Effect of Plasma Treatment Frequency on the Activation of Polymer Particles
AU - Abourayana, Hisham M.
AU - Milosavljević, Vladimir
AU - Dobbyn, Peter
AU - Dowling, Denis P.
N1 - Publisher Copyright:
© 2017, Springer Science+Business Media New York.
PY - 2017/7/1
Y1 - 2017/7/1
N2 - This study investigates the influence of treatment frequency (1–150 kHz) on the atmospheric plasma activation of both silicone and polyethylene terephthalate (PET) particles. These polymer particles with diameters in the range 3–5 mm, were treated using either helium or helium/oxygen gas mixtures, in a barrel atmospheric plasma system. The level of polymer particles activation was monitored using water contact angle measurements. The effect of plasma treatment frequency on barrel heating was monitored using an infrared thermographic camera, the maximum barrel temperature after 15 min treatment was found to be 98 °C at a frequency of 130 kHz. Optical emission spectroscopy was used as a diagnostic tool to monitor changes in atomic and molecular species spectral intensity with experimental conditions, as well as a change in electron energy distribution function. Electrical characterisation studies demonstrated an increase in plasma power with increasing frequency, in the range investigated. X-ray photoelectron spectroscopy analysis indicate an increase of oxygen content on polymer surfaces after plasma treatment. For silicone particles, the minimum polymer water contact angle was obtained by using a frequency of 130 kHz. After 15 min treatment time, the water contact angle decreased from 141° to 11°. While for PET particles the optimum treatment frequency was found to be 70 kHz, resulting in a water contact angle decreased from 94° to 32°. This lower frequency was used due to the partial melting of the PET (Tg of 80 °C), when treated at the higher frequency.
AB - This study investigates the influence of treatment frequency (1–150 kHz) on the atmospheric plasma activation of both silicone and polyethylene terephthalate (PET) particles. These polymer particles with diameters in the range 3–5 mm, were treated using either helium or helium/oxygen gas mixtures, in a barrel atmospheric plasma system. The level of polymer particles activation was monitored using water contact angle measurements. The effect of plasma treatment frequency on barrel heating was monitored using an infrared thermographic camera, the maximum barrel temperature after 15 min treatment was found to be 98 °C at a frequency of 130 kHz. Optical emission spectroscopy was used as a diagnostic tool to monitor changes in atomic and molecular species spectral intensity with experimental conditions, as well as a change in electron energy distribution function. Electrical characterisation studies demonstrated an increase in plasma power with increasing frequency, in the range investigated. X-ray photoelectron spectroscopy analysis indicate an increase of oxygen content on polymer surfaces after plasma treatment. For silicone particles, the minimum polymer water contact angle was obtained by using a frequency of 130 kHz. After 15 min treatment time, the water contact angle decreased from 141° to 11°. While for PET particles the optimum treatment frequency was found to be 70 kHz, resulting in a water contact angle decreased from 94° to 32°. This lower frequency was used due to the partial melting of the PET (Tg of 80 °C), when treated at the higher frequency.
KW - Atmospheric plasma
KW - Barrel reactor
KW - Frequency
KW - Surface activation
UR - https://www.scopus.com/pages/publications/85015930768
U2 - 10.1007/s11090-017-9810-1
DO - 10.1007/s11090-017-9810-1
M3 - Article
SN - 0272-4324
VL - 37
SP - 1223
EP - 1235
JO - Plasma Chemistry and Plasma Processing
JF - Plasma Chemistry and Plasma Processing
IS - 4
ER -